Quote:
Originally Posted by Allan Kelsey
|
That's some real odd breakage.
The angled breaks are characteristic of brittle materials twisted off, that is exactly what a piece of chalk will look like if you twist the ends until it breaks in the middle. However, rod bolts aren't near that brittle, note the larger piece that is bent but not fractured. And the other end that is squared off is also puzzling, why would single bolts break in two places?
Are you sure those are ARP? There have been fake arp bolts found in the marketplace made of substandard material. It is hard to tell from the picture, but when I have used arp, they are almost jewel like in finish, not rough at all.
Will be very interesting when you open it up.