and fuchs deform, they don't crack
Porsche 911 Picture
Here is one that will dampen that rumor. Could be a repo, but fuch's still crack regardless. |
||
05-30-2011, 10:27 AM
|
|
|
muck-raker
Join Date: Jan 2009
Location: Coastal PNW
Posts: 3,059
|
oh, SCHITT.
Clearly fakes....(just kidding.)
__________________
STONE '88 Cabriolet, using EP Slick 20w50 partial synthetic Snake Oil...just as Rommel intended.  Deny Everything; Admit Nothing; and Always Make Counter-accusations 
|
||
|
05-30-2011, 10:35 AM
|
|
|
Registered
Join Date: Oct 2004
Posts: 15,612
|
I doubt that is a forged wheel.
|
||
|
05-30-2011, 10:57 AM
|
|
|
Registered
Join Date: Mar 2001
Location: Marysville Wa.
Posts: 22,456
|
if you magnify the pic, it looks like it has a raised lip like a steel wheel.
__________________
https://www.instagram.com/johnwalker8704 8009 103rd pl ne Marysville Wa 98270 206 637 4071 |
||
|
05-30-2011, 11:15 AM
|
|
|
Registered
Join Date: Feb 2008
Posts: 1,438
|
Fuchs fatigue crack around bolt holes, the grain pattern of the break looks like cast aluminum, besides if the crack did result in a break it wouldn't shatter the entire center like the picture shows. Forged aluminum is ductile and this was a brittle failure.
Like John Walker noted: steel rim!
__________________
Paul Abbott Weber service specialist www.PerformanceOriented.com |
||
|
05-30-2011, 12:27 PM
|
|
|
Registered
Join Date: Jun 2000
Posts: 3,444
|
Could be a 17" Fuchs made from a 16X6 rim.
I can see how it would catastrophically fail, being subjected to loads far exceeding what a 16X6 would see, plus after being welded, and being so many years old. |
||
|
05-30-2011, 12:36 PM
|
|
|
|
RETIRED
|
I sent an email to the editor....maybe they will respond.
__________________
1983/3.6, backdate to long hood 2012 ML350 3.0 Turbo Diesel |
||
|
05-30-2011, 02:11 PM
|
|
Da cab